ANALISA PENGARUH WAKTU PENAHANAN PADA PROSES PACK CARBURIZING TERHADAP KEKERASAN BAJA KARBON RENDAH ST 37
Article Sidebar
Published:
Feb 26, 2021
Keywords:
Pack Carburizing, Effect of Holding Time on Hardness, Low Carbon Steel.
Main Article Content
Abstract
This study aims to analyze the hardness of low carbon steel ST 37 which received pack carburizing treatment with coconut shell charcoal. In this study, the specimens were divided into ten parts, which is five specimens carried out by pack carburizing, and other five parts by pack carburing and hardening and quenching followed by with oil. The carbon medium was coconut shell charcoal with a percentage of 10.60% volatile, 76.32% carbon, 13.08% ash and CaCO3 as a catalyst. The pack carburizing process is carried out at temperature of 9500C with i holding time of 2 hours, 4 hours, 6 hours, 8 hours, and 10 hours, as the oil quenching media hardness testing is carried out to determine how hard the specimen surface is. And the remit are this research was conducted at the material testing laboratory, Department of Mechanical Engineering, Sriwijaya State Polytechnic.
Downloads
Download data is not yet available.
Article Details
How to Cite
Apriatun, A., Taufikurahman, T., & Sundari, E. (2021). ANALISA PENGARUH WAKTU PENAHANAN PADA PROSES PACK CARBURIZING TERHADAP KEKERASAN BAJA KARBON RENDAH ST 37. MACHINERY: Jurnal Teknologi Terapan, 2(1), 23–27. https://doi.org/10.5281/zenodo.4748538
Section
Articles
The Authors submitting a manuscript do so on the understanding that if accepted for publication, copyright of the article shall be assigned to MACHINERY: Jurnal Teknologi Terapan as publisher of the journal. Copyright encompasses rights to reproduce and deliver the article in all form and media, including reprints, photographs, microfilms, and any other similar reproductions, as well as translations.
MACHINERY: Jurnal Teknologi Terapan and the Editors make every effort to ensure that no wrong or misleading data, opinions or statements be published in the journal. In any way, the contents of the articles and advertisements published in MACHINERY: Jurnal Teknologi Terapan are the sole responsibility of their respective authors and advertisers.
References
Abidah Faizatul Aidha, Drastiawati Sukma Novi, 2019. Analisa SS 400 Hasil Carburizing Media Arang Tempurung Kelapa BaCO3 Dengan Variasi Temperatur Pemanasan dan Holding Time Ditinjau Dari Pengujian Kekerasan dan Struktur Mikro, Jurnal Teknik Mesin. Volume 07 Nomor 02 Hal. 1-8, Fakultas Teknik Universitas Negeri Surabaya.
Dermawan Adi, Mustaqim, Shiddiq Fajar, 2017. Pengaruh Temperatur Carburizing Pada Pack Carburizing Terhadap Sifat-sifat Mekanik Baja S 21 C, Volume 14 no 1, Universitas Pancasakti Tegal.
Effendi, S., Firdaus, Karmin, Romli, Homzah, O.F., & Fernandes, Y.E. (2020). Effects of Carburizing Processes on Nodular Cast Iron with Variations in Temperature, Time and Cooling System. J. Phys.: Conf. Ser. 1500 012087. doi: http://10.1088/1742-6596/1500/1/012087
Gunawan Eddy, 2017. Analisa Pengaruh Temperatur Terhadap Sifat Mekanik dan Struktur Mikro Pada Baja Karbon Rendah (ST 41) Dengan Metode Pack Carburizing. Teknik Mesin, Teknika : Engineering and Sains Jurnal Volume 1 Nomor 2 hal 117-124, Fakultas Teknik Universitas Maarif Hasyim Latif, Sidoarjo Indonesia.
Karmin, 2009. Pengendalian Proses Pengerasan Baja Dengan Metode Quenching, Jurnal Austenit, Volume 1 Nomoe 2, Politeknik Negeri Padang.
Mirantie Dwiharsanti, Winda Sri Jaman, dan Shinta Virdhia, 2016. Perencanaan Eksperimen Baja Karbon Rendah Hasil Proses Pack Carburizing Dengan Metode Eksperimen Faktorial. Jurnal Riset Industri volume 10 nomor 2 hal 92-97. Bandung.
Wattimena W. M. E., Loihenapessy Jendri, 2014. Pengaruh Holding Time dan Quenching Terhadap Kekerasan Baja Karbon ST 37 Menggunakan Arang Batok Biji Pala. Jurnal Teknologi, Volume 11, No 1 Hal 1163-1171, Fakultas Teknik Universitas Pattimura.
Dermawan Adi, Mustaqim, Shiddiq Fajar, 2017. Pengaruh Temperatur Carburizing Pada Pack Carburizing Terhadap Sifat-sifat Mekanik Baja S 21 C, Volume 14 no 1, Universitas Pancasakti Tegal.
Effendi, S., Firdaus, Karmin, Romli, Homzah, O.F., & Fernandes, Y.E. (2020). Effects of Carburizing Processes on Nodular Cast Iron with Variations in Temperature, Time and Cooling System. J. Phys.: Conf. Ser. 1500 012087. doi: http://10.1088/1742-6596/1500/1/012087
Gunawan Eddy, 2017. Analisa Pengaruh Temperatur Terhadap Sifat Mekanik dan Struktur Mikro Pada Baja Karbon Rendah (ST 41) Dengan Metode Pack Carburizing. Teknik Mesin, Teknika : Engineering and Sains Jurnal Volume 1 Nomor 2 hal 117-124, Fakultas Teknik Universitas Maarif Hasyim Latif, Sidoarjo Indonesia.
Karmin, 2009. Pengendalian Proses Pengerasan Baja Dengan Metode Quenching, Jurnal Austenit, Volume 1 Nomoe 2, Politeknik Negeri Padang.
Mirantie Dwiharsanti, Winda Sri Jaman, dan Shinta Virdhia, 2016. Perencanaan Eksperimen Baja Karbon Rendah Hasil Proses Pack Carburizing Dengan Metode Eksperimen Faktorial. Jurnal Riset Industri volume 10 nomor 2 hal 92-97. Bandung.
Wattimena W. M. E., Loihenapessy Jendri, 2014. Pengaruh Holding Time dan Quenching Terhadap Kekerasan Baja Karbon ST 37 Menggunakan Arang Batok Biji Pala. Jurnal Teknologi, Volume 11, No 1 Hal 1163-1171, Fakultas Teknik Universitas Pattimura.