PENGARUH PERLAKUAN PANAS NORMALIZING TERHADAP KEKUATAN TARIK PADA BAJA TULANGAN DEFORM PASCA KEBAKARAN

Authors

  • Rayel Prialdo Politeknik Negeri Sriwijaya
  • Tri Widagdo Politeknik Negeri Sriwijaya
  • Soegeng Witjahjo Politeknik Negeri Sriwjaya

DOI:

https://doi.org/10.5281/zenodo.4748520

Keywords:

Reinforcing Steel, Tensile Strength, Normalizing

Abstract

The purpose of this study was to determine the effect of normalizing treatment on tensile strength, yield stress and strain of reinforcing steel after fire. Normalizing treatment was carried out at a temperature of 800 ° C with a holding time of 25 minutes and compared the results of post fire reinforcing steel with after normalizing treatment. The goals of the normalizing process vary widely. Normalizing can increase or decrease the strength and hardness of steel, depending on the heat treatment and mechanical properties of the steel prior to the normalizing process. But in general the purpose of the normalizing process is to increase the machinability, grain-structure refinement, homogenization, and regulate or modify the residual stress that exists in steel. From the results of the tensile test after normalizing, the highest tensile strength value was obtained in the specimens cooled with water at 600 ° C at 597.85 N / mm² and the lowest value at 400 ° C with air at 443.9 N / mm². The largest yield stress value was at 600 ° C with water at 416.28 N / mm² and the lowest value at 800 ° C with air at 318.243 N / mm². The greatest value of strain was at 800 ° C with water at 31.66% and the smallest strain at 400 ° C with air at 21.67%.

Author Biographies

Rayel Prialdo, Politeknik Negeri Sriwijaya

Teknik Mesin Produksi dan Perawatan

Tri Widagdo, Politeknik Negeri Sriwijaya

Teknik Mesin Produksi dan Perawatan

Soegeng Witjahjo, Politeknik Negeri Sriwjaya

Teknik Mesin Produksi dan Perawatan

References

Bambang Pratowo, 2012. Analisis tegangan tarik dan kekerasan besi beton bertulang pasca kebakaran. Momentum, Vol.8, No.1 UNWAHAS

Subagiyo, Sarjiyana, Wirawan, 2016. Analisis kekuatan tarik besi beton ulir berdasarkan diameternya. Seminar nasional terapan teknologi POLINEMA 2016

Badan Standarisasi Nasional, 2014. Baja Tulangan Beton. Jakarta : Badan Standarisasi Nasional.

Muchtar Karokaro, 2016. Pengaruh Normalizing Ulang Terhadap Sifat Kelelahan Baja DIN 42 Mn V7. Jurusan Teknik Mesin FTI-ITS Surabaya.

Deri Dwi Darmawan, 2018. Pengujian dan struktur mikro baja karbon rendah yang telah mengalami proses perlakuan panas ( Heat Treatment ). Universitas Bandar Lampung Teknik Mesin Vol. 5, No.2 (2018).

Haris budiman, 2016. Analisa pengujian tarik (tensile test) padabaja ST37 dengan alat bantu ukur load cell. Jurnal J-Ensitec Vol. 03, No.01 FT-Universitas Majalengka

Hermansyah, Syahroni, ST, Anton Aryanto, M.Eng, 2014. Analisa kuat tarik Besi BJTP Ø 16 mm yang ada di pasaran Rokan Hulu (Study kasusbesi BJTP Ø 16 mm besi SS, GS dan HHS). Universitas pengaraian.

Riyanto Hery Nugroho, 2014. Analisis sifat mekanik kekuatan baja tulangan polos hasil proses perlakuan panas fasa ganda. Info Teknik Volume 15 No. 2 Desember 2014 (175-188) Politeknik Negeri Malang.

Downloads

Published

2021-02-26