ANALISA PENGARUH VARIASI MEDIA PACK CARBURIZING TERHADAP KEKERASAN BAJA AISI 1020

Article Sidebar

PDF
Published: Jun 21, 2021
DOI: https://doi.org/10.5281/zenodo.5812366
Keywords:
Uji Kekerasan, Pack Carburizing, ANOVA

Main Article Content

Rafi Banar Adi
Mahasiswa Sarjana Terapan Teknik Mesin Produksi dan Perawatan, Politeknik Negeri Sriwijaya
Moch Yunus
Politeknik Negeri Sriwijaya
Suparjo .
Politeknik Negeri Sriwijaya

Abstract

Baja AISI 1020 termasuk kedalam kategori baja karbon rendah dengan komposisi C 0.20%, Si 0.24%, Mn 0.01067%, P 0.000025% dan S 0.000024%. Berdasarkan kandungan karbonnya memungkinkan baja ini dikeraskan permukaannya dengan proses pack carburizing dan quenching. Penelitian ini menggunakan metode eksperimen dengan 1 spesimen raw material dan 9 spesimen untuk proses pack carburizing. Variasi media pack carburizing yang digunakan pada penelitian ini yaitu batubara, arang kayu gelam dan arang tempurung kelapa. Proses pack carburizing dilakukan pada suhu 9000C dengan holding time 2 jam serta proses quenching menggunakan air PAM. Hasil pengujian didapatkan nilai rata-rata spesimen raw material sebesar 78.5 HRB. Peningkatan nilai kekerasan tertinggi pada proses pack carburizing yaitu pada media batubara dengan rata-rata nilai kekerasan 111.0066667 HRB dan komposisi C sebesar 0.457%. Peningkatan nilai rata-rata kekerasan terendah yaitu pada media kayu gelam sebesar 87.93 HRB dan komposisi C sebesar 0.249%, sedangkan peningkatan nilai rata-rata kekerasan pada media tempurung kelapa sebesar 101.09 HRB. Dari hasil pengujian kekerasan nilai rata-rata tertinggi yaitu pada spesimen dengan menggunakan media batubara.

Downloads

Download data is not yet available.

Article Details

How to Cite
Banar Adi, R., Yunus, M., & ., S. (2021). ANALISA PENGARUH VARIASI MEDIA PACK CARBURIZING TERHADAP KEKERASAN BAJA AISI 1020. MACHINERY: Jurnal Teknologi Terapan, 2(2), 110–115. https://doi.org/10.5281/zenodo.5812366
Issue
Vol. 2 No. 2 (2021): Machinery:02022021
Section
Articles
Creative Commons License

This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

The Authors submitting a manuscript do so on the understanding that if accepted for publication, copyright of the article shall be assigned to MACHINERY: Jurnal Teknologi Terapan as publisher of the journal. Copyright encompasses rights to reproduce and deliver the article in all form and media, including reprints, photographs, microfilms, and any other similar reproductions, as well as translations. 

MACHINERY: Jurnal Teknologi Terapan and the Editors make every effort to ensure that no wrong or misleading data, opinions or statements be published in the journal. In any way, the contents of the articles and advertisements published in MACHINERY: Jurnal Teknologi Terapan are the sole responsibility of their respective authors and advertisers.

References

Budi, Esmar, Hadi Nasbey, Setia Budi, Erfan Handoko, Suharmanto Puji, dan Sinansari. 2012. “Kajian Pembentukan Karbon Aktif Berbahan Arang Tempurung Kelapa.” Seminar Nasional Fisika 62–66.

Dermawan, Adi, Mustaqim, dan Fajar Sidiq. 2017. “Pengaruh Temperatur Carburizing Pada Proses Pack Carburizing Terhadap Sifat – Sifat Mekanis Baja S 21 C.” Engineering 14(1):7–14.

Ghozali, Imam. 2009. “Aplikasi Analisis Multivariate dengan Program SPSS “. Semarang : UNDIP.

Hafni. 2015. “Pengaruh Waktu Tahan Proses Pack Carburizing Pada Baja Karbon Rendah Dengan Menggunakan Calcium Carbonat Dan Arang Tempurung Kelapa, Di Tinjau Dari Kekerasan.” Jurnal Teknik Mesin 5(2):108–12.

Poertadji, Suhardjo, Muhammad Hikam, dan Nukman. 2006. “Pengaruh Aglomerasi Air-Minyak Sawit Terhadap.” 7(3):68–74.

Prayitno, Tibertius A., dan Gentur J. P. Sutapa. 2007. “Kualitas Arang Kayu Gelam ( Melaleuca Cajuputi ) ( Quality of Charcoal Made from Gelam Wood ( Melaleuca Cajuputi )).” 141–52.

Setiono, Yud. 2012. "Penelitian Sifat Fisis Dan Mekanis Baja Karbonisasi Arang Kayu Sengon". Tugas Akhir. Fakultas Teknik, Jurusan Teknik Mesin, UNIVERSITAS MUHAMMADIYAH SURAKARTA.