PENGARUH DRUMUS OIL SEBAGAI MEDIA PENDINGIN TERHADAP PENINGKATAN KEKERASAN DAN TRANFORMASI FASA PADA PROSES PENGERASAN BAJA AMUTIT
Keywords:
Hardness, tempering, mechanical properties.Abstract
Engineering process technology is basically an effort to optimize the use of natural resources effectively and efficiently in order to provide maximum benefit for the benefit of human life. Amutit steel is one of the low alloy steel which is identical to AISI O1 standard. This steel hardness can be increased through a heat treatment process that allows used for industrial purposes as cold work tool steels as well as other purposes. In this research the process of hardening, the steel is heated to a temperature of 8200 C and then cooled rapidly using a coolant emulsion (dromus oil with water). To reduce brittle properties and improve the ductility, the steel is then heated again at a temperature of 4000 C and held for one hour and cooled slowly in the furnace. The results amutit hardening of steel using a coolant with a mixture ratio variations dromus oil with water, after tempering highest hardness is 590 HV, obtained using dromus oil emulsion with water 1:30 ratio while using oil as quenching media produced 544 HV hardness.
Downloads
Downloads
Published
Issue
Section
License
The Authors submitting a manuscript do so on the understanding that if accepted for publication, Authors retain copyright and grant the AUSTENIT right of first publication with the work simultaneously licensed under a Creative Commons Attribution-ShareAlike License that allows others to share the work with an acknowledgment of the work's authorship and initial publication in this journal.
AUSTENIT, the Editors and the Advisory International Editorial Board make every effort to ensure that no wrong or misleading data, opinions or statements be published in the journal. In any way, the contents of the articles and advertisements published in AUSTENIT are the sole responsibility of their respective authors and advertisers.