PENGARUH MEDIA PENDINGIN KADAR AIR GARAM TERHADAP KEKERASAN PADA HASIL PENGELASAN SMAW BAJA KARBON RENDAH
DOI:
https://doi.org/10.5281/zenodo.7247133Keywords:
Welding, Low Carbon Steel, Hardness, BrineAbstract
Welding in the world of production and maintenance is widely used usually for machine construction in various fields. One of the most widely used materials for machine construction is low carbon steel with a carbon content of 0.05% - 0.30%. In this study, we will provide heat treatment to low carbon steel through a welding process using a cooling medium with variations in salt content. The purpose of this study was to see the effect of heat treatment by welding process on low carbon steel with cooling media with variations in salt water content. The welding method used in this study is the SMAW welding method, with cooling media in the form of: sea water, salt water with variations in salt content (10%, 20%, 30%) with 3 samples for one cooling medium. The hardness test method used is the Rockwell hardness test with tests carried out by taking 5 points for one sample. After testing, it was concluded that the average hardness increased with increasing salt content in the salt solution with the results of the hardness test, namely, seawater cooling media with an average hardness value of 88.37 HRB, cooling media with a salt content of 10% an average value of 88.37 HRB. The hardness produced is 96.6 HRB, the cooling medium with 20% salt content has an average hardness value of 105.83 HRB, the cooling medium with 30% salt content has an average hardness value of 114.1 HRB.
Downloads
References
Khakim, A.L. 2020. Pengaruh Variasi Media Pendingin Pada Sifat Mekanis Baja Karbon Rendah Untuk AS Roda Sepeda Motor. Universitas Pancasakti Tegal.
Priyanto, I. 2017. Pengaruh Temperatur Media Pendingi (Air, Collant, Oli) Pada Pengelasam GMAW Terhadap Struktur Mikro, Kekuatan Tarik Dan Kekerasan Pada Baja ST 37. Universitas Negeri Semarang.
Rizal, Taufan. 2005. Pengaruh kadar garam dapur (NaCl) dalam media pendingin terhadap tingkat kekerasan pada proses pengerasan baja.
Santoso, Joko. 2006. Pengaruh Arus Pengelasan terhadap Kekuatan Tarik dan Ketangguhan Las GMAW dengan Elektroda E7018.
Trihutomo, P. 2015. Analisa Kekerasan Pada Pisau Berbahan Baja Karbon Menengah Hasil Proses Hardening Dengan Media Pendingin Yang Berbeda
Widiyono, E, Gatot Dwi P, Atria P, Winarto, dan Dimas Wisnu Wardana. 2018. Analisa Pengaruh Penambahan Garam Di Media Pendingin Air Terhadap Kekuatan Tarik Dan Struktur Mikro Pada Baja Karbon AISI 1050. InstitutfTeknologifSepuluhfNopemberfSurabaya.
Yuri, S, Sofyan Djamil dan M Sobrom Yamin Lubis. 2016. Pengaruh Media Pendingin Pada Proses Hardening Material Baja S45C. Jakarta: Universitas Tarumanegara.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2022 Authors and Publisher
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.
The Authors submitting a manuscript do so on the understanding that if accepted for publication, copyright of the article shall be assigned to MACHINERY: Jurnal Teknologi Terapan as publisher of the journal. Copyright encompasses rights to reproduce and deliver the article in all form and media, including reprints, photographs, microfilms, and any other similar reproductions, as well as translations.Â
MACHINERY: Jurnal Teknologi Terapan and the Editors make every effort to ensure that no wrong or misleading data, opinions or statements be published in the journal. In any way, the contents of the articles and advertisements published in MACHINERY: Jurnal Teknologi Terapan are the sole responsibility of their respective authors and advertisers.