ANALISIS KEBOCORAN SAMBUNGAN LAS PIPA SANITARY SS 316L YANG DI RENDAM DALAM LARUTAN pH 4
DOI:
https://doi.org/10.36257/machinery.v6i3.10569Keywords:
sanitary pipe SS 316L, acid solution, pH 4, welding, corrosionAbstract
This study aims to analyze the cause of leakage in SS 316L sanitary pipes used for food additive distribution. The leakage is suspected to be caused by corrosion due to exposure to the acidic environment. The research was conducted experimentally using 12 samples subjected to different treatments: no welding, argon welding, and electric welding using NSN-309L/E 309-16 and NSN-316/E 309-16 electrodes. All samples were immersed for 24 hours in a pH 4 solution and tested using the gravimetric method to measure mass loss due to erosion. The results showed that pH 4 acid solution significantly caused mass reduction in the pipes, with the highest erosion occurring in electric welding joints. The highest erosion percentage, 2.99%, was found in samples welded with NSN-309L/E 309-16 electrodes, while unwelded samples experienced only 0.21% erosion. The validity of the data was tested and confirmed based on the comparison between the calculated r-value and the critical r-table value. The conclusion indicates that the welding method influences the pipe’s susceptibility to corrosion, with electric welding posing a higher risk than argon welding in acidic environments.
Downloads
References
[1] Arini, Aziza Ayu. “Analisis Risiko Kebocoran Pada Tangki Penyimpanan Asam Sulfat Menggunakan Metode Quantitative Risk Analysis (Qra)”. Politeknik Perkapalan Negeri Surabaya, Surabaya, Indonesa, Final Rep, Feb 13, 2024 Available: Leakage Risk Analysis of Sulfuric Acid Storage Tank's Using Method Quantitative Risk Analysis (QRA)
[2] Husaini, Mirza, Masri Ali, Mahmud M. Nizar. “Analisis Kegagalan Daerah Lasan Pipa Stainless Steel Sebagai Media Reboiler Pabrik Pupuk”. Universitas Syiah Kuala. Banda Aceh. PROCEEDING; Seminar Nasonal Tahunan Teknik Mesin XIII (SNTTM XIII). Depok, 15-16 Oktober 2014. Available: https://prosiding.bkstm.org/prosiding/2014/AM-40.pdf
[3] Putra, Herdiansyah. “Pengaruh Media Pendingin Sesudah Pengelasan Terhadap Sifat Mekanis Stainless Steel 316”. Universitas Islam Riau, Pekanbaru, Indonesia, Final Rep, Feb 13, 2024 Available: https://repository.uir.ac.id/8964/1/143310114.pdf
[4] Mariah, Yuni. “Studi Korosi Plat Baja Material Kapal Terhadap Salinitas Dan Derajat Keasaman (Ph) Di Pelabuhan Pengasinan Pertamina Jakarta”. Akademi Maritim Djadajat. Jurnal Indonesia Sosial Sains.
Vol. 2 No. 3 Maret 2021. Available: https://www.researchgate.net/publication/350375756_Studi_Korosi_Plat_Baja_Material_Terhadap_Salinitas_dan_Derajat_Keasaman_PH_di_Pelabuhan_Pengasinan_Pertamina_Jakarta
[5] Nugroho Sri, Rusnaldy. Änalisis Kebocoran Pipa Reformer Di Sebuah Perusahaan Petrokimia”. Universitas Diponegoro. Jurnal Teknik Mesin ROTASI. Vol. 16 No. 2 April 2014: 27-31. Available : https://ejournal.undip.ac.id/index.php/rotasi/article/download/8428/6941
[6] Antara, Nengah Ludra. “Pencegahan Akibat Terjadinya Karat Pada Pipa Boiler,” Politeknik Negeri Bali.JURNAL LOGIC. VOL. 13. NO. 3. NOPEMBER 2013, Available : https://ojs.pnb.ac.id/index.php/LOGIC/article/view/331/282
[7] Kiagus M. Rizky Khadafi, Hendradinata, Fenoria Putri, Utami Ogi Meita. “Analisis Kegagalan Pipa Embedded Pada PLTU TE 3X10 MW”. Politeknik Negeri Sriwijaya. MACHINERY; Jurnal Teknik Mesin VOL. 5 NO. 2, Juni 2024. ISSN: 2776-673X. Available: https://jurnal.polsri.ac.id/index.php/machinery/article/view/7122/3226
[8] Dewi Idamayanti, Beny Bandanadjaja, Achyarsyah Mochamad. “Analisis Kegagalan Pipa Aisi 316L Pada Lingkungan Lepas Pantai”. Politeknik Manufaktur Negeri Bandung. STEMAN 2016. ISBN 978- 979-17047-6-2. Available: https://www.academia.edu/37132046/ANALISIS_KEGAGALAN_PIPA_AISI_316L_PADA_LINGKUNGAN_LEPAS_PANTAI
[9] Andrika, Yogi. “Pengaruh Asam Organik Hasil Pyrolysis Cangkang Kelapa Sawit Sebagai Pereduksi Scale Pada Pipa Distribusi”. Universitas Islam Riau, Pekanbaru, Indonesia, Final Rep, Feb 13, 2024. Available: https://repository.uir.ac.id/17898/1/153210510.pdf
[10] Sam, Alimuddin. “Analisa Kecepatan Korosi Pipa Galvanis Pada Tanah Dengan Tingkat Kehalusan Yang Berbeda”. Universitas Tadulako, Palu. Jurnal SMARTek. Available: https://media.neliti.com/media/publications/221539-analisisa-kecepatan-korosi-pipa-galvanis.pdf
[11] Triharto, Dandi Panggih, “Studi Ketahanan Korosi Material Sus 316L, Sus 317L, Sus 329J Dan Hc-276 Dalam Larutan Asam Asetat Yang Mengandung Ion Bromida,” M.S. thesis, Fakultas Teknik, Universitas Indonesia, Depok, Indonesia, 2010. [Onlne]. Available: https://lib.ui.ac.id/detail?id=131646&lokasi=lokal
[12] Elisabeth Kinanthi Pengestuti, Darmawan Petrus. “Analisis Kadar Abu dalam Tepung Terigu dengan Metode Gravimetri”. Universitas Setia Budi, Surakarta. Jurnal Kimia dan Rekayasa. Volume 2 Nomor 1 Tahun 202. Available: https://kireka.setiabudi.ac.id/index.php/kireka/article/download/22/17/69
[13] Sinta Novita. Ediman Ginting. Astuti, Widi. “Analisis Laju Korosi Dan Kekerasan Pada Stainless Steel
304 Dan Baja Nikel Laterit Dengan Variasi Kadar Ni (0, 3, Dan 10% Ni) Dalam Medium Korosif”. Universitas Lampung. Jurnal Teori dan Aplikasi Fisika. Vol. 06, No. 01, Januari 2018. Available: https://jtaf.fmipa.unila.ac.id/index.php/jtaf/article/view/163/160
[14] Pangestu. Dedek Arya. Hastuti, Sri. Pramono Catur, dkk. “Pengaruh Waktu Proses Thermal Spray Aluminium Terhadap Laju Korosi dan Struktur Morfologi Baja AISI 1020”. Politeknik Negeri Sriwijaya. MACHINERY; Jurnal Teknik Mesin VOL. 5 NO. 3, Oktober 2024. ISSN: 2776-673X. Available: https://jurnal.polsri.ac.id/index.php/machinery/article/view/8636/3455
[15] Wahyuni Noor. Available: https://qmc.binus.ac.id/2014/11/01/u-j-i-v-a-l-i-d-i-t-a-s-d-a-n-u-j-i-r-e-l-i-a-b-i-l-i-t-a-s/
[16] Yuli Purwanto, Saputra Dwi Luhur Ibnu. “Pengukuran Laju Korosi Pada Kondisi Asam Material Stainless Steel Yang Mengalami Pengelasan”. Pusat Teknologi Limbah Radioaktif-BATAN. Tangerang Selatan. PROSIDING; Hasil Penelitian dan Kegiatan PTLR TAhun 2020. Available: https://inis.iaea.org/records/s3pje- sdm03
Downloads
Published
Issue
Section
License
Copyright (c) 2025 Authors and Publisher
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.
The Authors submitting a manuscript do so on the understanding that if accepted for publication, copyright of the article shall be assigned to MACHINERY: Jurnal Teknologi Terapan as publisher of the journal. Copyright encompasses rights to reproduce and deliver the article in all form and media, including reprints, photographs, microfilms, and any other similar reproductions, as well as translations.Â
MACHINERY: Jurnal Teknologi Terapan and the Editors make every effort to ensure that no wrong or misleading data, opinions or statements be published in the journal. In any way, the contents of the articles and advertisements published in MACHINERY: Jurnal Teknologi Terapan are the sole responsibility of their respective authors and advertisers.